Trench MIS device with active trench corners and thick bottom oxide

ABSTRACT

Trench MOSFETs including active corner regions and a thick insulative layer at the bottom of the trench are disclosed, along with methods of fabricating such MOSFETs. In an exemplary embodiment, the trench MOSFET includes a thick insulative layer centrally located at the bottom of the trench. A thin gate insulative layer lines the sidewall and a peripheral portion of the bottom surface of the trench. A gate fills the trench, adjacent to the gate insulative layer. The gate is adjacent to the sides and top of the thick insulative layer. The thick insulative layer separates the gate from the drain conductive region at the bottom of the trench yielding a reduced gate-to-drain capacitance making such MOSFETs suitable for high frequency applications.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is related to Application No. 09/927,320 filed on the same date as this application, and to application Ser. No. 09/591,179, filed Jun. 8, 2000, each of which is incorporated herein by reference in its entirety.

FIELD OF THE INVENTION

This invention relates to trench metal-insulator-semiconductor (MIS) devices and in particular to trench MOSFETs that are suitable for high frequency operation.

BACKGROUND

Some metal-insulator-semiconductor (MIS) devices include a gate located in a trench that extends downward from the surface of a semiconductor substrate (e.g., silicon). The current flow in such devices is primarily vertical and, as a result, the cells can be more densely packed. All else being equal, this increases the current carrying capability and reduces the on-resistance of the device. Devices included in the general category of MIS devices include metal-oxide-semiconductor field effect transistors (MOSFETs), insulated gate bipolar transistors (IGBTs), and MOS-gated thyristors.

Trench MOSFETs, for example, can be fabricated with a high transconductance (g_(m,max)) and low specific on resistance (R_(on)), which are important for optimal linear signal amplification and switching. One of the most important issues for high frequency operation, however, is reduction of the MOSFET internal capacitances. The internal capacitances include the gate-to-drain capacitance (C_(gd)), which is also called the feedback capacitance (C_(rss)), the input capacitance (C_(iss)), and the output capacitance (C_(oss)).

FIG. 1 is a cross-sectional view of a conventional n-type trench MOSFET 10. In MOSFET 10, an n-type epitaxial (“N-epi”) layer 13, which is usually grown on an N⁺ substrate (not shown), is the drain. N-epi layer 13 may be a lightly doped layer, that is, an N⁻ layer. A p-type body region 12 separates N-epi layer 13 from N⁺ source regions 11. Current flows vertically through a channel (denoted by the dashed lines) along the sidewall of a trench 19. The sidewall and bottom of trench 19 are lined with a thin gate insulator 15 (e.g., silicon dioxide). Trench 19 is filled with a conductive material, such as doped polysilicon, which forms a gate 14. Trench 19, including gate 14 therein, is covered with an insulative layer 16, which may be borophosphosilicate glass (BPSG). Electrical contact to source regions 11 and body region 12 is made with a conductor 17, which is typically a metal or metal alloy. Gate 14 is contacted in the third dimension, outside of the plane of FIG. 1.

A significant disadvantage of MOSFET 10 is a large overlap region 18 formed between gate 14 and N-epi layer 13, which subjects a portion of thin gate insulator 15 to the drain operating voltage. The large overlap limits the drain voltage rating of MOSFET 10, presents long term reliability issues for thin gate insulator 15, and greatly increases the gate-to-drain capacitance, C_(gd), of MOSFET 10. In a trench structure, C_(gd) is larger than in conventional lateral devices, limiting the switching speed of MOSFET 10 and thus its use in high frequency applications.

One possible method to address this disadvantage is described in the above-referenced application Ser. No. 09/591,179 and is illustrated in FIG. 2. FIG. 2 is a cross-sectional view of a trench MOSFET 20 with an undoped polysilicon plug 22 near the bottom of trench 19. MOSFET 20 is similar to MOSFET 10 of FIG. 1, except for polysilicon plug 22, which is isolated from the bottom of trench 19 by oxide layer 21 and from gate 14 by oxide layer 23. The sandwich of oxide layer 21, polysilicon plug 22, and oxide layer 23 serves to increase the distance between gate 14 and N-epi layer 13, thereby decreasing C_(gd).

In some situations, however, it may be preferable to have a material even more insulative than undoped polysilicon in the bottom of trench 19 to minimize C_(gd) for high frequency applications.

One possible method to address this issue is described in the above-referenced Application No. [Attorney Docket No. M-11671 US] and is illustrated in FIG. 3. FIG. 3 is a cross-sectional view of a trench MOSFET 30 with a thick insulative layer 31 near the bottom of trench 19. MOSFET 30 is similar to MOSFET 10 of FIG. 1 and MOSFET 20 of FIG. 2. In MOSFET 30, however, only the sidewall of trench 19 is lined with thin gate insulator 15 (e.g., silicon dioxide). Unlike MOSFET 10 of FIG. 1, a thick insulative layer 31 (e.g., silicon dioxide) lines the bottom of trench 19 of MOSFET 30 of FIG. 3. Thick insulative layer 31 separates gate 14 from N-epi layer 13. This circumvents the problems that occur when only thin gate insulator 15 separates gate 14 from N-epi layer 13 (the drain) as in FIG. 1. Thick insulative layer 31 provides a more effective insulator than is achievable with polysilicon plug 22 as shown in FIG. 2. Thick insulative layer 31 decreases the gate-to-drain capacitance, C_(gd), of MOSFET 30 compared to MOSFET 20 of FIG. 2.

The solution of FIG. 3 has a thin gate oxide region 24 between body region 12 and thick insulative layer 31. This is because the bottom interface of body region 12 and the top edge of thick insulative layer 31 are not self-aligned. If body region 12 extends past the top edge of thick insulative layer 31, MOSFET 30 could have a high on-resistance, R_(on), and a high threshold voltage. Since such alignment is difficult to control in manufacturing, sufficient process margin can lead to significant gate-to-drain overlap in thin gate oxide regions 24. Thin gate region 24 also exists in MOSFET 20 of FIG. 2, between body region 12 and polysilicon plug 22. Thus, C_(gd) can still be a problem for high frequency applications. Accordingly, a trench MOSFET with decreased gate-to-drain capacitance, C_(gd), and better high frequency performance is desirable.

SUMMARY

In accordance with the present invention, a metal-insulator-semiconductor (MIS) device includes a semiconductor substrate including a trench extending into the substrate from a surface of the substrate. A source region of a first conductivity type is adjacent to a sidewall of the trench and to the surface of the substrate. A body region of a second conductivity type opposite to the first conductivity type is adjacent to the source region and to the sidewall and to a first portion of a bottom surface of the trench. A drain region of the first conductivity type is adjacent to the body region and to a second portion of the bottom surface of the trench. The trench is lined with a first insulative layer at least along the sidewall that abuts the body region and at least along the first portion of the bottom surface that abuts the body region. The trench is also lined with a second insulative layer along the second portion of the bottom surface of the trench. The second insulative layer is coupled to the first insulative layer, and the second insulative layer is thicker than the first insulative layer.

In an exemplary embodiment of a fabrication process for such an MIS device, a trench including a sidewall, a corner surface, and a central bottom surface is formed in a substrate. A thick insulative layer is deposited on the central bottom surface. A thin insulative layer is formed on the sidewall and on the corner surface. A gate is formed around and above the thick insulative layer and adjacent to the thin insulative layer in the trench, so as to form an active corner region along at least a portion of the corner surface.

In one embodiment, the thick insulative layer is deposited using a mask layer that is deposited and etched to expose a central portion of the bottom surface of the trench. The thick insulative layer is deposited and etched to form an exposed portion of the mask layer on the sidewall, leaving a portion of the thick insulative layer on the central portion of the bottom surface of the trench. The mask layer is removed, exposing the sidewall and the corner surface of the trench, while leaving the portion of the thick insulative layer on the central portion of the bottom surface of the trench.

The thick insulative layer separates the trench gate from the drain conductive region at the bottom of the trench, while the active corner regions minimize the gate-to-drain overlap in thin gate insulator regions. This results in a reduced gate-to-drain capacitance, making MIS devices in accordance with the present invention, such as trench MOSFETs, suitable for high frequency applications.

BRIEF DESCRIPTION OF THE DRAWINGS

This invention will be better understood by reference to the following description and drawings. In the drawings, like or similar features are typically labeled with the same reference numbers.

FIG. 1 is a cross-sectional view of a conventional trench MOSFET.

FIG. 2 is a cross-sectional view of a trench MOSFET with a polysilicon plug at the bottom of the trench.

FIG. 3 is a cross-sectional view of a trench MOSFET with a thick insulative layer at the bottom of the trench.

FIG. 4 is a cross-sectional view of one embodiment of a trench MOSFET in accordance with the present invention.

FIGS. 5A-5P are cross-sectional views illustrating one embodiment of a process for fabricating a trench MOSFET in accordance with the present invention.

FIG. 6 is a cross-sectional view of an alternative embodiment of a trench MOSFET in accordance with the present invention.

FIG. 7 is a cross-sectional view of an alternative embodiment of a trench MOSFET in accordance with the present invention.

DETAILED DESCRIPTION OF THE INVENTION

FIG. 4 is a cross-sectional view of one embodiment of a trench MOSFET 40 in accordance with the present invention. In MOSFET 40, an n-type epitaxial (“N-epi”) layer 13, which may be an N⁻ layer and is usually grown on an N⁺ substrate (not shown), is the drain. A p-type body region 12 separates N-epi layer 13 from N⁺ source regions 11. Body region 12 is diffused along the sidewall of a trench 19, past a corner region 25, and partially long the bottom of trench 19. Current flows vertically through a channel (denoted by the dashed lines) along the sidewall and around corner region 25 of trench 19.

The sidewall and corner region 25 of trench 19 are lined with a thin gate insulator 15 (e.g., silicon dioxide). An oxide plug 33 is centrally located in the bottom of trench 19. Trench 19 is filled with a conductive material, such as doped polysilicon, which forms a gate 14. Gate 14 extends into corner region 25 of trench 19, between oxide plug 33 and gate insulator 15. Trench 19, including gate 14 and oxide plug 33 therein, is covered with an insulative layer 16, which may be borophosphosilicate glass (BPSG). Electrical contact to source regions 11 and body region 12 is made with a conductor 17, which is typically a metal or metal alloy. Gate 14 is contacted in the third dimension, outside of the plane of FIG. 4.

The trench MOSFET of FIG. 4 uses oxide plug 33 to separate gate 14 from N-epi layer 13, thereby decreasing the gate-to-drain capacitance, C_(gd). Having the channel extend around corner region 25 to the bottom of the trench precludes significant gate-to-drain overlap in thin gate oxide regions (i.e., see thin gate oxide regions 24 in FIG. 3) because the diffusion of body region 12 can be very well controlled through corner region 25. Since lateral diffusion is six to ten times slower than vertical diffusion, the pn junction between body region 12 and N-epi layer 13 can be made to coincide with the transition between thin gate insulator 15 and oxide plug 33. Thus, oxide plug 33 and active corner region 25 minimize the gate-to-drain capacitance, C_(gd), with minimum impact on on-resistance, R_(on), yielding a trench MOSFET 40 useful for high frequency applications.

FIGS. 5A-5P are cross-sectional views illustrating one embodiment of a process for fabricating a trench MOSFET, such as MOSFET 40 of FIG. 4, in accordance with the present invention. As shown in FIG. 5A, the process begins with a lightly-doped N-epi layer 413 (typically about 8 μm thick) grown on a heavily doped N⁺ substrate (not shown). A pad oxide 450 (e.g., 100-200 Å) is thermally grown by dry oxidation at 950° C. for 10 minutes on N-epi layer 413. As shown in FIG. 5B, a nitride layer 452 (e.g., 200-300 Å) is deposited by chemical vapor deposition (CVD) on pad oxide 450. As shown in FIG. 5C, nitride layer 452 and pad oxide 450 are patterned to form an opening 453 where a trench 419 is to be located. Trench 419 is etched through opening 453, typically using a dry plasma etch, for example, a reactive ion etch (RIE). Trench 419 may be about 0.5-1.2 μm wide and about 1-2 μm deep.

A second pad oxide 454 (e.g., 100-200 Å) is thermally grown on the sidewall and bottom of trench 419, as shown in FIG. 5D. A thick nitride layer 456 (e.g., 1000-2000 Å) is deposited conformally by CVD on the sidewall and bottom of trench 419 as well as on top of nitride layer 452, as shown in FIG. 5E. Nitride layer 456 is etched using a directional, dry plasma etch, such as an RIE, using etchants that have high selectivity for nitride layer 456 over pad oxide 450. The nitride etch leaves spacers of nitride layer 456 along the sidewall of trench 419, while exposing pad oxide 454 in the central bottom portion of trench 419, as shown in FIG. 5F. It is possible that nitride layer 456 may be overetched to such a degree that nitride layer 452 is removed from the top of pad oxide 450.

As shown in FIG. 5G, a thick insulative layer 433 (e.g., 2-4 μm) is then deposited. The deposition process is chosen, according to conventional deposition techniques such as CVD, to be non-conformal, filling trench 419 and overflowing onto the top surface of N-epi layer 413. Thick insulative layer 433 may be, for example, a low temperature oxide (LTO), a phosphosilicate glass (PSG), a BPSG, or another insulative material.

Insulative layer 433 is etched back, typically by performing a wet etch, using an etchant that has high selectivity for insulative layer 433 over nitride layer 456. Insulative layer 433 is etched back into trench 419 until only about 0.1-0.2 μm remains in trench 419, as shown in FIG. 5H.

Nitride layer 456 is removed, typically by performing a wet etch, using an etchant that has high selectivity for nitride layer 456 over insulative layer 433. Pad oxide 450 is also removed, typically by a wet etch. This wet etch will remove a small, but insignificant portion of insulative layer 433, leaving the structure as shown in FIG. 5I.

In some embodiments, an approximately 500 Å sacrificial gate oxide (not shown) can be thermally grown by dry oxidation at 1050° C. for 20 minutes and removed by a wet etch to clean the sidewall of trench 419. The wet etch of such a sacrificial gate oxide is kept short to minimize etching of insulative layer 433.

As shown in FIG. 5J, a thin gate insulator 415 (e.g., about 300-1000 Å thick) is then formed on the sidewall of trench 419 and the top surface of N-epi layer 413. Thin gate insulator 415 may be, for example, a silicon dioxide layer that is thermally grown using a dry oxidation at 1050° C. for 20 minutes.

As shown in FIG. 5K, a conductive material 456 is deposited by CVD, possibly by low pressure CVD (LPCVD), to fill trench 419 and overflow past the topmost surface of thin gate insulator 415. Conductive material 456 may be, for example, an in-situ doped polysilicon, or an undoped polysilicon layer that is subsequently implanted and annealed, or an alternative conductive material. Conductive material 456 is etched, typically using a reactive ion etch, until the top surface of material 456 is approximately level with the top of N-epi layer 413, thereby forming gate 414, as shown in FIG. 5L. In an n-type MOSFET, gate 414 may be, for example, a polysilicon layer with a doping concentration of 10²⁰ cm⁻³. In some embodiments, conductive material 456 may be etched past the top of trench 419, thereby recessing gate 414 to minimize the gate-to-source overlap capacitance.

Using known implantation and diffusion processes, p-type body regions 412 are formed in N-epi layer 413 as shown in FIG. 5M. Body regions 412 are diffused such that the PN junctions between p-type body regions 412 and the remainder of N-epi layer 413 are located near the interface between thick insulative layer 433 and thin gate insulator 415. This interface occurs at a location along the bottom of trench 419, where the diffusion of body regions 412 is dominated by lateral diffusion under trench 419 rather than vertical diffusion deeper into N-epi layer 413, making control of the diffusion of body regions 412 easier.

Using known implantation and diffusion processes, N⁺ source regions 411 are formed in N-epi layer 413 as shown in FIG. 5N.

As shown in FIG. 5O, an insulative layer 416, which may be borophosphosilicate glass (BPSG), is deposited by CVD on the surfaces of N-epi layer 413 and gate 414. Insulative layer 416 is etched, typically using a dry etch, to expose portions of p-type body regions 412 and N⁺ source regions 411, as shown in FIG. 5P. Electrical contact to body regions 412 and source regions 411 is made with a conductor 417, which is typically a deposited (e.g., by physical vapor deposition) metal or metal alloy. Electrical contact to gate 414 is made in the third dimension, outside of the plane of FIG. 5P. Electrical contact to the drain (not shown) is made to the opposite surface of the N⁺ substrate (not shown) on which N-epi layer 413 is grown.

This method thus allows incorporation of thick insulative layer 433, centrally positioned at the bottom of trench 419, to decrease C_(gd) with minimal undesirable effects or manufacturing concerns. For example, stress effects from growing a thick oxide in the concave bottom of trench 419 are avoided by depositing the oxide rather than thermally growing it. In addition, by keeping corner region 25 active (i.e., part of the MOSFET channel), the gate-to-drain overlap in thin gate oxide regions 24 of MOSFET 30 (see FIG. 3) are avoided. This minimizes C_(gd).

FIG. 6 is a cross-sectional view of an alternative embodiment of a trench MOSFET 60 in accordance with the present invention. MOSFET 60 has many similarities to MOSFET 40 of FIG. 4. In particular, the sidewall and corner region 25 of trench 19 are lined with thin gate insulator 15, while oxide plug 33 is centrally located in the bottom of trench 19. In FIG. 6, however, the PN junctions between body regions 12 and N-epi layer 13 are not located as near to the interface between oxide plug 33 and thin gate insulator 15 as in MOSFET 40 of FIG. 4. In fact, the location of the PN junctions between body regions 12 and N-epi layer 13 can vary. As discussed above with reference to FIG. 5M, body regions 412 are formed using known implantation and diffusion techniques. The structure of MOSFET 60 of FIG. 6 can be fabricated by varying the diffusion conditions associated with the diffusion of body regions 12 so that diffusion stops before body regions 12 reach the interface of oxide plug 33.

MOSFET 60 of FIG. 6 exhibits reduced gate-to-drain capacitance, C_(gd), compared to MOSFET 10 of FIG. 1, MOSFET 20 of FIG. 2, and MOSFET 30 of FIG. 3. MOSFET 10 of FIG. 1 has a large C_(gd) due to thin gate insulator 15 throughout overlap region 18. MOSFET 20 of FIG. 2 and MOSFET 30 of FIG. 3 have large C_(gd) due to thin gate insulator 15 throughout thin gate oxide regions 24, since regions 24 may be large due to the fast nature of vertical diffusion. The extent of thin gate oxide region 24 in MOSFET 60 of FIG. 6, however, can be minimized since the diffusion of body regions 12 in thin gate oxide region 24 will be dominated by lateral diffusion under trench 19, instead of vertical diffusion deeper into N-epi layer 13.

FIG. 7 is a cross-sectional view of an alternative embodiment of a trench MOSFET 70 in accordance with the present invention. MOSFET 70 has many similarities to MOSFET 40 of FIG. 4. In particular, the sidewall and corner region 25 of trench 19 are lined with thin gate insulator 15, while oxide plug 33 is centrally located in the bottom of trench 19. In MOSFET 40 of FIG. 4, oxide plug 33 may increase the on-resistance (R_(on)) of MOSFET 40 due to an increase in the spreading resistance in the accumulation layer at the bottom of trench 19. MOSFET 70 of FIG. 7, however, includes a high doping region 73 at the bottom of trench 19 to help spread current more effectively and minimize pinching of body region 12. High doping region 73 also helps self-align the PN junction between p-type body regions 412 and N-epi layer 413 to the edge of thick insulative layer 433, during the diffusion process shown in FIG. 5M. High doping region 73 is formed in N-epi layer 13. High doping region 73 may be created by implanting an n-type dopant, such as arsenic or phosphorous, after trench 19 is etched as shown in FIG. 5C, after pad oxide 454 is formed as shown in FIG. 5D, or after nitride layer 456 is etched as shown in FIG. 5F. Thus, oxide plug 33 minimizes gate-to-drain capacitance, C_(gd), and high doped region 73 minimizes on-resistance, R_(on), yielding a trench MOSFET 70 well-suited for high frequency applications.

The foregoing embodiments are intended to be illustrative and not limiting of the broad principles of this invention. Many additional embodiments will be apparent to persons skilled in the art. For example, the structures and methods of this invention can be used with any type of metal-insulator-semiconductor (MIS) device in which it is desirable to form an insulating layer between a trench gate and a region outside the trench, while minimizing the gate-to-drain overlap regions. Also, various insulative or conductive materials can be used where appropriate, and the invention is also applicable to p-type MOSFETs. The invention is limited only by the following claims. 

1. A metal-insulator-semiconductor device, comprising: a semiconductor substrate including a trench extending into said substrate from a surface of said substrate; a source region of a first conductivity type adjacent to a sidewall of said trench and to said surface; a body region of a second conductivity type opposite to said first conductivity type adjacent to said source region and to said sidewall and to a first portion of a bottom surface of said trench; and a drain region of said first conductivity type adjacent to said body region and to a second portion of said bottom surface of said trench, wherein said trench is lined with a first insulative layer at least along said sidewall that abuts said body region and at least along said first portion of said bottom surface that abuts said body region, and wherein said trench is lined with a second insulative layer at least along said second portion of said bottom surface of said trench, said second insulative layer being coupled to said first insulative layer and said second insulative layer being thicker than said first insulative layer.
 2. The MIS device of claim 1, further comprising a gate region coupled to said first insulative layer and said second insulative layer within said trench.
 3. The MIS device of claim 2, wherein said gate region comprises polysilicon.
 4. The MIS device of claim 1, further including a high conductivity region of said first conductivity type formed in said drain region adjacent to at least said second portion of said bottom surface of said trench.
 5. The MIS device of claim 1, wherein said first insulative layer extends to the interface between said first portion of said bottom surface and said second portion of said bottom surface.
 6. The MIS device of claim 5, wherein said body region extends to the interface between said first portion of said bottom surface and said second portion of said bottom surface.
 7. The MIS device of claim 5, wherein said body region extends to a first distance along said first portion of said bottom surface of said trench.
 8. The MIS device of claim 1, wherein said first insulative layer comprises an oxide.
 9. The MIS device of claim 1, wherein said second insulative layer comprises an oxide.
 10. The MIS device of claim 1, wherein said second insulative layer comprises a multi-layer insulative layer.
 11. The MIS device of claim 1, wherein said MIS device comprises a MOSFET.
 12. A trench-gated MOSFET, comprising: a semiconductor substrate including a trench extending into said substrate from a surface of said substrate; a source region of a first conductivity type adjacent to a sidewall of said trench and to said surface; a body region of a second conductivity type opposite to said first conductivity type adjacent to said source region and to said sidewall and to a peripheral portion of a bottom surface of said trench; a drain region of said first conductivity type adjacent to said body region and to a central portion of said bottom surface of said trench, wherein said trench is lined with a first insulative layer at least along said sidewall that abuts said body region and at least along said peripheral portion of said bottom surface that abuts said body region, and wherein said trench is lined with a second insulative layer at least along said central portion of said bottom surface of said trench, said second insulative layer being coupled to said first insulative layer and said second insulative layer being thicker than said first insulative layer; and a gate region coupled to said first insulative layer and said second insulative layer within said trench.
 13. The trench-gated MOSFET of claim 12, wherein said gate region comprises polysilicon.
 14. The trench-gated MOSFET of claim 12, further including a high conductivity region of said first conductivity type formed in said drain region adjacent to at least said central portion of said bottom surface of said trench.
 15. The trench-gated MOSFET of claim 12, wherein said first insulative layer extends to the interface between said peripheral portion of said bottom surface and said central portion of said bottom surface.
 16. The trench-gated MOSFET of claim 15, wherein said body region extends to the interface between said peripheral portion of said bottom surface and said central portion of said bottom surface.
 17. The trench-gated MOSFET of claim 15, wherein said body region extends to a first distance along said peripheral portion of said bottom surface of said trench.
 18. The trench-gated MOSFET of claim 12, wherein said first insulative layer comprises an oxide.
 19. The trench-gated MOSFET of claim 12, wherein said second insulative layer comprises an oxide.
 20. The trench-gated MOSFET of claim 12, wherein said second insulative layer comprises multi-layer insulative layer.
 21. A trench-gated MOSFET, comprising: a semiconductor substrate including a trench extending into said substrate from a first surface of said substrate, said trench including a sidewall, a corner surface, and a central bottom surface; a source region of a first conductivity type adjacent to said sidewall of said trench and to said first surface; a body region of a second conductivity type opposite to said first conductivity type adjacent to said source region and to said sidewall and to said corner surface of said trench; a drain region of said first conductivity type adjacent to said body region and to said central bottom surface of said trench, wherein said trench is lined with a first insulative layer at least along said sidewall that abuts said body region and at least along said corner surface that abuts said body region, and wherein said trench is lined with a second insulative layer at least along said central bottom surface of said trench, said second insulative layer being coupled to said first insulative layer and said second insulative layer being thicker than said first insulative layer; and a gate region coupled to said first insulative layer and said second insulative layer within said trench, so as to form an active corner region along at least a portion of said corner surface.
 22. The trench-gated MOSFET of claim 21, further including a high conductivity region of said first conductivity type formed in said drain region adjacent to at least said central bottom surface of said trench.
 23. The trench-gated MOSFET of claim 21, wherein said first insulative layer extends to the interface between said corner surface and said central bottom surface.
 24. The trench-gated MOSFET of claim 23, wherein said body region extends to the interface between said corner surface and said central bottom surface.
 25. The trench-gated MOSFET of claim 23, wherein said body region extends to a first distance along said corner surface of said trench. 